Description

1.1 This specification covers steel sheet, produced by the Twin-Roll Cast Process (see Appendix X2) and zinc-coated (galvanized) by the hot-dip process in coils and cut lengths.

Note 1 – See Appendix X2 for a description of the Twin-Roll Cast process.

1.2 The product is produced in various zinc coating weights [masses] or coating designations as shown in Table 1.

1.3 Product furnished under this specification shall conform to the applicable requirements of the latest issue of Specification A924/A924M unless otherwise provided herein.

1.4 The product is available in a number of designations, grades and classes and in the two following general categories that are designed to be compatible with different application requirements.

1.4.1 Steels with mandatory chemical requirements and typical mechanical properties.

1.4.2 Steels with mandatory chemical requirements and mandatory mechanical properties.

1.5 This material is available in the following sizes:

1.5.1 Thickness – up to 0.078 in. [2.0 mm]

1.5.2 Width – up to 79 in. [2000 mm]

1.6 The text of this specification references notes and footnotes that provide explanatory material. These notes and footnotes, excluding those in tables and figures, shall not be considered as requirements of this specification.

1.7 This specification is applicable to orders in either inch-pound units (as A1063) or SI units (as A1063M). Values in inch-pound and SI units are not necessarily equivalent. Within the text, SI units are shown in brackets. Each system shall be used independently of the other.

1.8 Unless the order specifies the “M“ designation (SI units), the product shall be furnished to inch-pound units.

1.9 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

TABLE 1 Weight [Mass] of Coating Requirements^A^, ^B^, ^C

Note – Use the information provided in 8.1.2 to obtain the approximate coating thickness from the coating weight [mass].

		Minimum Requirement
		Triple-Spot Test		Single-Spot Test
Inch-Pound Units
Type	Coating Designation	Total Both Sides, oz/ft²	One Side, oz/ft²	Total Both Sides, oz/ft²
Zinc	G01^C	no minimum	no minimum	no minimum
	G30	0.30	0.10	0.25
	G40	0.40	0.12	0.30
	G60	0.60	0.20	0.50
	G90	0.90	0.32	0.80
	G100	1.00	0.36	0.90
	G115	1.15	0.40	1.00
	G140	1.40	0.48	1.20
	G165	1.65	0.56	1.40
	G185	1.85	0.64	1.60
SI Units
Type	Coating Designation	Total Both Sides, g/m²	One Side, g/m²	Total Both Sides, g/m²
Zinc	Z001^C	no minimum	no minimum	no minimum
	Z90	90	30	75
	Z120	120	36	90
	Z180	180	60	150
	Z275	275	94	235
	Z305	305	110	275
	Z350	350	120	300
	Z450	450	154	385
	Z500	500	170	425
	Z550	550	190	475
	Z600	600	204	510

^A The coating designation number is the term by which this product is specified. Because of the many variables and changing conditions that are characteristic of continuous hot-dip coating lines, the zinc coating is not always evenly divided between the two surfaces of a coated sheet; nor is it always evenly distributed from edge to edge. However, the minimum triple-spot average coating weight (mass) on any one side shall not be less than 40 % of the single-spot requirement.

^B As it is an established fact that the atmospheric corrosion resistance of zinc coated sheet products is a direct function of coating thickness (weight (mass)), the selection of thinner (lighter) coating designations will result in almost linearly reduced corrosion performance of the coating. For example, heavier galvanized coatings perform adequately in bold atmospheric exposure whereas the lighter coatings are often further coated with paint or a similar barrier coating for increased corrosion resistance. Because of this relationship, products carrying the statement “meets ASTM A1063/A1063Mrequirements“ should also specify the particular coating designation.

^C No minimum means that there are no established minimum requirements for triple- and single-spot tests.